MPI Matco

1-800 975-8273

FIT30 15
Two Component Methacrylate

 

Ideal for composite bonding, the FIT range product line offers low-temperature curing reactions and minimal shrinkage, which protects composite resins from bond line read-through and stresses. With high thixotropic properties for high gap filling, FIT structural adhesives reduce dispensing time and adhesive waste, enhancing operational efficiencies while lowering overall costs. FIT30 product line is ideal for all your structural applications for marine market. With high strength and enhanced fatigue resistance, Bostik’s FIT product line can replace conventional mechanical fastenings, such as welds, rivets, screws and bolts for the assembly of all inserts onto composite. Additionally, these adhesives enable uniform bonds without stress points or damage to thin aluminum panels and to composites.

Key Features

  • Fast curing
  • Non-sag, application on vertical surfaces
  • Excellent environmental resistance
  • Minimal surface preparation

Application

Optimum qualities are obtained at room temperature, ideally between 18°C and 28°C without post-curing.

For Use with

  • Recommended Adhesive Gun : DM2X400
  • Matching static mixer : ADH_MHACF1018

Packaging

FIT 30 15 adhesive is available in 50ml and 490ml

  • FIT 30 15 50ml cartridges require the use of ADH_MH5416 static mixer
  • FIT 30 15 490ml cartridges require the use of ADH_MHACF1018 Static mixer

Range of application

The FIT30 15 is recommended for the following substrates:

Metals
Composites
Plastics
Steel
Polyester
PVC
Stainless Steel
Vinylester
PS
Aluminium
Epoxy
ABS
Galvanized steel
Acrylic (Elium)
PC
PMMA

Product Characteristics

System
Two component 1:10 Volume Ratio
Polymerization
Room Temperature

Adhesive Properties

Physical Properties Resin
Appearance
Off-white
Density
1.07
Viscosity @ 23°C
350 000 – 600 0001
Type
Non-sag
Curing Properties
Open Time [min]
6 - 8
Fixture time @ 23°C [min]
12 - 15
Full Cure [hours]
24
Mechanical Properties
Lap Shear strength on GFRP
Glass Reinforced Fiber Polymer
DF6
Tensile Strength at break [MPa] ISO 527-1A
15 - 17
Tensile Modulus [MPa] ISO 527-1A
1000 - 1200
Hardness [Shore D]
70 - 80
% elongation at break ISO 527-1A
25 - 30

Adhesive Selection Guide

Product Key Features-specifity Mix Ratio
(Vol.)
Viscosity Open Time(1)
(mins)
Fixture Time(1)
(mins)
Elongation
(%)
Lap Shear Strength
(Mpa) AL/FRP
Modulus
(Mpa)
FIT30 5
Very Fast Setting
10 / 1
Non-sag
2 - 3
5-6
25 - 35
17(CF) - 7(DF)
1000 - 1200
FIT 30 15
Structural, High strength and
High modulus. Fast curing.
10 / 1
Non-sag
6 - 8
12 -15
25 - 35
19(CF) - 7(DF)
1000 - 1200
FIT30 45
Structural, High Modulus.
Medium curing time.
High gap filling.
10 / 1
Non-sag
20 - 30
45 - 60
25 - 35
19(CF) - 7(DF)
1000 - 1200
FIT30 90
Slow Curing. Vertical application.
Gelcoat direct bonding.
High gap filling.
1/10
Non-sag
55 - 65
75 - 100
25 - 35
15(CF) - 7(DF)
1000 - 1200
FIT30 120
Extended open time.
Gelcoat direct bonding.
Very high gap filling.
10 / 1
Non-sag
80 -100
120 -150
25 -35
17(CF) - 9(DF)
800 -1000
(CF) Cohesive Failure
(DF) Delamination Failure
(1) @23°C