Black Mamba FHG
MS60 Universal

 

MS60 Black Mamba FHG is made of mono-component MS polymer adhesives. These adhesives react with the humidity in the air and offer optimal sealing even under pressure. The main advantage of this product is the speed at which skin can form as well as the curing speed in which 100% of the active matter reacts.

It is recommended to use this product in temperatures varying between -40 and 140°C but optimal qualities are achieved between 5 and 35°C. Shrinkage is at 1% and the elongation at break can go up to 400% which enables it to resist impacts, vibrations and peeling. It is resistant to water, UV exposure, yellowing and aggressive environments such as alkaline, diluted acids, polar solvents, oils and more.

Range of Application

Black Mamba FHG High Tack is recommended for the following substrates:

  • Metal – aluminum, steel and other alloys
  • Technical plastics – ABS, PMMA, PVC and more
  • Glass and laminated glass Composites
  • Powdered paint applications

Product Characteristics

  • Easy to apply by manual or compressed air gun extrusion
  • Polymerization at room temperature.
  • Joints: Adhesive applied within 10mins with spatula at     20°C & 50% R.H.
  • Bonding: Substrate applied within 15mins at 20°C &            50% R.H.
  • Does not need primer

Colours

  • Grey opaque 
  • White opaque 
  • Black opaque

Adhesive Properties

Physical Properties
Tensile Strength at break [MPa]
2.4
Hardness [Shore A]
60
Elongation at break
380%
Liquid Properties
Specific gravity @ 20°C [g/ cm3]
1.55 - 1.58
Viscosity @ 25°C (Pa.s)
160 - 220
Yield Point (Pa)2
630 – 650
Curing Properties
Skin formation time [min] @ 20°C & 50% R.H.
10 -15
Cure Speed [mm/24h] @ 20°C & 50% R.H.
5
Temperature Range [°C]
-40 to 140